Present work deals with the dielectric and electrochemical properties of PMMA/TiO2 and PMMA/TiO2@Clay nanocomposite prepared via a simple sol -gel method followed by ultrasonication. With pore diameters of 16.657 angstrom, ternary nanocomposites have an increased specific surface area of 28.88 m2/g. The significant dielectric properties are observed for PMMA/TiO2 and PMMA/TiO2@Clay nanocomposite with the highest dielectric constant epsilon ' of 3.66 x 103 and 1.45 x 103 and maximum dielectric loss epsilon '' of 1.7 and 1.9 at 1 kHz respectively. The PMMA/TiO2 nanocomposite exhibits the highest sigma ac conductivity of 1.29 x 10-4 S/m and 6.85 x 10-2 S/m, whereas; the PMMA/TiO2@Clay nanocomposite demonstrates the highest sigma ac conductivity of 1.47 x 10-4 S/m and 1.84 x 10-2 S/m at 1 kHz and 3 MHz, respectively. The manufactured device's highest specific capacitance is 364.13 F/g, which corresponds to an energy density of 129.26 Wh/kg and a power density of 2913.04 W/kg. Even after 5000 CV cycles, a 97 % capacitance retention is reported in the cyclic stability. The present work proves its virtue and competency towards superior energy storage applications.
Copyright:Copyright [2024]. All efforts have been made to respect the copyright to the best of our knowledge. Inadvertent omissions, if brought to our notice, stand for correction and withdrawal of document from this repository.