Abstract:
The present paper reports the effective utilization of marble sludge powder (MSP) for the recovery of potash values from waste mica scrap using chlorination roasting-water leaching method. Characterization studies indicated the presence of dolomite as the major mineral phase in MSP, whereas muscovite and quartz were observed in the mica sample. The acid leaching studies suggest a maximum of 22% potash recovery under conditions: 4 M H(2)SO(4)acid, particle size of similar to 100 mu m, stirring speed of 600 r/min, leaching temperature of 75 degrees C, and leaching time of 90 min. The chlorination roasting-water leaching process was adopted to achieve the lowest level of 80%-90% potash recovery. The optimum conditions for the recovery of similar to 93% potash from mica (similar to 8.6wt% K2O) requires 900 degrees C roasting temperature, 30 min roasting time, and 1:1:0.75 mass ratio of mica: MSP: NaCl. The roasting temperature and amount of NaCl are found to be the most important factors for the recovery process. The reaction mechanism suggests the formation of different mineral phases, including sylvite (KCl), wollastonite, kyanite, and enstatite, during roasting, which were confirmed by X-ray diffraction (XRD) analyses and scanning electron microscopy (SEM) morphologies. The MSP-blended NaCl additive is more effective for potash recovery compared with the other reported commercial roasting additives.