Extraction of Cu and Cr from a spent Cu-Cr catalyst: Recovery enhancement through mechanical activation

Abstract

Treatment process for a spent Cu-Cr catalyst (Cu 42.4% and 36.2% Cr) was described. The catalyst contained cuprous chromite (CuCrO2), cupric chromite (CuCr2O4) and copper sub-oxide (Cu8O) phases. High energy ball milling reduced the mean particle size from 9.4 to 1.7 mu m along with simultaneous increase in surface area by about 63%. Cuprous chromite phase is selectively mechanically activated. Sulfuric acid leaching and alkali roasting followed by water leaching techniques were employed for Cu and Cr recovery respectively. Un-milled catalyst showed maximum 67% Cu extraction by varying H2SO4 concentration (0.94 M-3.75 M) and leaching temperature (ambient - 150 degrees C) whereas a 5 h milled sample resulted in 90% Cu extraction under the conditions of 1.31 M H2SO4, 20 g/L S:L ratio, 80 degrees C. Cr recovery was examined by varying NaOH amount, roasting temperature and time. More than 90% Cr extraction was achieved when a milled sample was roasted with 100 wt% NaOH at 850 degrees C for 2 h. Cr recovery from the Cu-leached residue was comparatively more than that obtained from raw milled sample. The leach residue after Cr recovery was nearly pure CuO which can be recycled for Cu recovery. A conceptual flow-sheet for the recovery of both metals was described. (C) 2013 Elsevier B.V. All rights reserved.