Preliminary results of growth of thin diamond film in a recently installed 3 kW capacity microwave plasma activated CVD (MW-PACVD) system are being reported. The films were deposited on Si (100) substrate at 850A degrees C using methane and hydrogen mixture at 1 center dot 5 kW MW power. The grown polycrystalline films were characterized by micro-Raman, transmission electron microscope (TEM), spectrophotometer and atomic force microscope (AFM). The results were compared with that of a thicker diamond film grown elsewhere in a same make MW-PACVD system at relatively higher power densities. The presence of a sharp Raman peak at 1332 cm (-aEuro parts per thousand 1) confirmed the growth of diamond, and transmission spectra showed typical diamond film characteristics in both the samples. Typical twin bands and also a quintuplet twinned crystal were observed in TEM, further it was found that the twinned region in thin sample composed of very fine platelet like structure.
Copyright:Copyright [2012]. All efforts have been made to respect the copyright to the best of our knowledge. Inadvertent omissions, if brought to our notice, stand for correction and withdrawal of document from this repository.