Abstract:
The effect of calcination temperature on the physico-chemical characterization of manganese nodule leached residue (MNLR) and water-washed manganese nodule leached residue (WMNLR) has been investigated on the basis of chemical analysis, XRD, TG-DTA, FTIR, surface hydroxyl groups, surface oxygen, reducing and oxidizing sites, surface area. XRD and IR confirm the presence of amorphous iron oxyhydroxides, delta-MnO2, which are converted to alpha-Fe2O3 and gamma-Mn2O3 phases above 400 degrees C of calcination, respectively. A solid solution of Fe2O3 and Mn2O3 is formed above 700 degrees C. The surface area, surface hydroxyl group, surface oxygen, reducing and oxidizing sites increase with the increase in calcination temperature up to 400 degrees C and then decrease with further rise in calcination temperature up to 700 degrees C. The catalytic activity of the sample towards H2O2 decomposition shows the similar trend as surface properties. A suitable Mn3+-Mn4+ couple favours H2O2 decomposition reaction. The activity has been correlated with various physico-chemical properties. (c) 2005 Elsevier Inc. All rights reserved.